Product Construction
Backing material PE foam
Type of adhesive tackified acrylic
Total thickness 800 µm
Color black/white
Properties / Performance Values
Elongation at break 250 %
Static shear resistance at 23°C good
Humidity resistance very good
Static shear resistance at 40°C good
Temperature resistance long term 80 °C
Temperature resistance short term 80 °C
Tack good
Tensile strength 8 N/cm
Ageing resistance (UV) good
Softener resistance medium
Adhesion to Values
Adhesion to Steel (initial) 17 N/cm
Adhesion to PE (initial) 2.7 N/cm
Adhesion to PC (after 14 days) 17 N/cm
Adhesion to PS (after 14 days) 17 N/cm
Adhesion to ABS (initial) 17 N/cm
Adhesion to PP (after 14 days) 5.5 N/cm
Adhesion to PET (after 14 days) 17 N/cm
Adhesion to Aluminium (after 14 days) 17 N/cm
Adhesion to PE (after 14 days) 2.8 N/cm
Adhesion to Aluminium (initial) 17 N/cm
Adhesion to ABS (after 14 days) 17 N/cm
Adhesion to PC (initial) 15 N/cm
Adhesion to PVC (initial) 17 N/cm
Adhesion to PS (initial) 15 N/cm
Adhesion to PET (initial) 12.5 N/cm
Adhesion to PP (initial) 2.8 N/cm
Adhesion to Steel (after 14 days) 17 N/cm
Adhesion to PVC (after 14 days) 17 N/cm
Additional Info
Liner variants:
PV0 brown glassine paper (71 µm)
PV10 red transparent PP film (120 µm)
PV15 blue PE film (100 µm)
Peel Adhesion:
immediate: foam splitting on Steel, Aluminium, ABS
after 14 days: foam splitting on Steel, Aluminium, ABS, PC, PS, PET, PVC
tesa® 62934 has been tested by TÜV Rheinland, Germany. The test confirms the longterm adhesion performance after IEC 61215 / 61646 climate tests and a 85°C temperature resistance. (TÜV report number 21209595).